1. Product features
Keep soft and elastic property under long time operation during -65°C~200°
Excellent electrical property and chemical stability
Water-resistance, ozone resistance, weatherable aging, non-corrosiveness, non-reactivity and environmentally friendly.
Low linear shrinkage, high transparency, excellent mould-releasing ability and easy operation
2. Product typical applications
Making precision mold, like polyurethane, epoxy resin;
Mapping the size of chemical materials, carbon fibrous composite materials and machine parts;
Duplicating artware and decoration made by POLYSTER, ER-OXY and PU foamex;
Making artistic and fancy candles and gypsum mould ;
Mould making of furniture and electronics
For making high hardness and long working life rubber pad printing head.
3. Product Technical Parameters
Project | Unit | Value | Test method | ||
Before | Component | A | B | ||
Appearance | Transparent fluid | Transparent fluid | Visual results | ||
Viscosity(25℃) | Pa·s | ≤80 | ≤1 | GB/T 2794-1995 | |
Mixture ratio | A:B | 10:1 | |||
Pot life, 25℃ | min | 80 | |||
Vulcanizing time,at 25℃ | h | 20 | |||
Vulcanizing time,at 60℃ | min | 50 | |||
Vulcanizing time,at 80℃ | min. | 40 | |||
After | Tensile strength | MPa | ≥5.5 | GB/T 528-2009 | |
elongation | % | ≥400 | GB/T 528-2009 | ||
Tear strength | kN/m | ≥15 | GB/T 529-2008 | ||
Linear shrinkage | % | ≤0.1 | |||
Shore A hardness | 40±3 | GB/T 531-1999 |
The above data only for reference.
(Sample preparation curing conditions: 24h*at room temperature ,80℃×60min)
4. Product Color
It is the transparent fluid after mixing A and B.
The color can be done according to client’s demand.
5. Usage and dosage
Premix: before using, mixing well A and B separately
Weigh: weigh A and B according to A: B = 10:1.
Mix: mixing the two components well, it is better to use the special rubber mixing equipment (like small planet stirrer). If mixing the rubber by hand, make sure the bottom and the sides of the drum are scraped well.
Defoaming: putting the mixed rubber in to the special equipment to defoaming under vacuum, or you can put the mixed rubber together with the special mixing equipment in the vacuum defoam equipment and defoaming. During the vacuum defoaming procession, the liquid level of the mixture will be higher 3-4 times than before. Then after the bubble broke, maintain the vacuum for 4-6 minutes. Finally release the vacuum.
Mould making: Liquid injection moulding(LIM) is suggested. Inject sizing material into moulding chamber, after 24hours at room temperature, then can get silicone rubber model. It can extend the mould working life after treating the vulcanized silicone rubber mould 2 hours under 80-100℃. To improve the molding efficiency, it also can be cured under the high temperature of 60℃-90℃
6. Matters to be attention
Specific materials, compound, vulcanizing agent and plasticizer will affect the vulcanization of JY131M including:
Organic tin and other metallo-organic compound
Silicone rubber with organic tin catalyzer
Sulfur, polysulfide, polysulfone or other sulfur-containing materials
Amine, ethyl carbamate or amine-containing materials
Unsaturated hydrocarbon plasticizer
Scaling powder remnant
If you don’t know whether the material (A) will affect the vulcanization, you can do a small compatibility test. If there has liquid or non-vulcanized material that exist in the A and the gel surface . it shows that it doesn’t have consistency and will hinder vulcanization.
The component A and component B are non-toxic. there is no need to take special preventive measures, it just needs general industrial hygiene.
The catalyzer is easily to be poisoned and lose activity, pls avoid contacting the nitrogen, phosphorus, sulphur compounds and heavy metals compounds, such as organic tin . Keep the utensil clean.
The operation period of the mixed JY-131M will be influenced by environment temperature. The operation period will be shorten at high temperature.
7. Package
Component A and Component B are packed in 200kg metal barrel and 20kg plastic drum separately, or other specification package.
8. Product storage and transportation
This product should be stored under the temperature of 0℃~30℃. The shelf life is 1 year under original packaging sealed condition. To be shipped according to the non-dangerous goods.